As a matter of fact Creo is now capable of saving and editing native solid works files without loosing the file structure. There are a few bugs...
Yes Cavist sold the rights to the Moldman machines because they wanted to focus on the manufacturing and molding process. You can work with Cavist...
You can easily make an ejection molded part with two different type finishes. The shinny one just have a high polish and the matte a rough or bead...
Can you put in any type of expansion joint? Not sure how the glycol system would be running here but you need to reduce the stress pushing up...
Here is a decent forum on flow rate vs pressure with some of the equations to get you going....
Flow rate will be a function of pressure. As the pressure drops so will the flow rate.
Obviously, not familiar with your design but we have used macromelt overmolding on a few different PCAs. Not wearable technology but generally...
Interesting! The problem with bearings is most are designed only for radial loads unless you get a thrust bearing or others that support axial...
I wouldn't use a hex coupling. The threads would probably catch unless you drill them out like robert suggested but that seems like a lot of work...
It has been awhile since I have worked with pressure vessels. I don't think it is wrong but can definitely be more complex but at low pressures...
What is the normal force that would be applied? Do you think a paint would hold up to continuous friction? Probably not unless the force is very...
This is actually a very good question. You need to understand the definitions of the properties pretty well. Cool question never seen it asked...
Greg, One question, have you not had a design review with the company that will do the injection molding on the design? I am not sure how things...
Davide, I would like to direct your attention to this article I stumbled across today and thought it was pretty informative and mostly like the...
Also, if you are not aware at Protlabs.com you can submit designs and have them quoted. Through this process they will check for any bad design or...
One important question I have before a response is what is the material going to be? Do you have a data sheet? Do you have any idea of where you...
I find these questions very hard to answer but I will try. I can answer the questions as simply as it is asked. Yes, it is possible to do some...
I am not aware of any that are free that work. I have heard pretty go results about anyDWG. It isn't free but there is a trial that lets you...
I would say go back to the basics. This is a simple problem that doesn't really need FEA. Derive the equations for a beam with fixed ends and two...
PVC is molded very successfully. This is what I would look into. Check mold for undercuts and/or insufficient draft. Decrease booster time....
Separate names with a comma.
▲